Spectra Aluminium Composite Panels With High Glossy For Art Building
Descrition:
Inspirited by themes from nature such as iridescent colors. The surface coated with a special high gloss painting, bring us a smooth and colorful feeling. Interaction between light and material, reflection, diffraction and absorption are the secrets of color effects in nature. Chameleon Aluminium Composite Panel shows fantasy decorative effects.
|
Raw material |
product specifications
|
|
Base material of aluminum panel:high strength aluminum alloy coils |
thickness:3-6mm,4mm is recommended |
|
PE core:non-toxic low density polythene |
width:1000-2000mm. 1220mm,1250mm,1500mm,2000mm are recommended
|
|
Surface coating:fluorocarbon coating,triple coating system |
length:maximum is up to5800mm,2440mm,3050mm,4050mm are recommended |
|
|
Thickness of aluminum sheet:0.2mm-0.5mm |
Features of MAXL Spectra Aluminium Composite Panel
1 The face will change as per change of lamp and visual angle
2 High Glossy,more than 85%.
3 Special visual decorations, such as art building, Ads Show, etc
Test Report
|
Coating |
Requirement |
Composite Panel |
Requirement |
|
coating rididity |
≥２Ｈ |
Length Deviation |
≤2mm |
|
Adhesive Force |
Cross-Cut Method Level 0 |
Width Deviation |
≤1mm |
|
Coating Flexibility |
≤2T |
Thickness Deviation |
≤0.1mm |
|
Durability |
≥5L/μm |
Diagonal Deviation |
≤3mm |
|
Boiling Water Resistance |
No change after 2 hours |
Edge Nonstraightness |
≤1mm/m |
|
Alkali Resistance |
No change |
Angularity |
≤5mm/m |
|
Acid Resistance |
No change |
Areal Density |
2.88kg/m2 |
|
Solvent Resistance |
No change |
Bending Strength |
≥60Mpa |
|
Washing Resistance |
No change after 10000 times |
Flexural Modulus |
≥15000Mpa |
|
|
Through Resistance |
≥5KN |
|
|
Shear Strength |
≥20Mpa |
||
|
180 Peeling Strength |
≥5N/mm |
||
|
Thermal Shock Resistance |
No Change |
||